Monel 505 Alloy: Product Description
Monel 505 is a high-strength nickel-copper alloy renowned for its excellent corrosion resistance and mechanical properties. It is primarily composed of 63% nickel, 31% copper, with trace amounts of iron (up to 2.5%), manganese (up to 1.5%), and titanium (0.35-0.85%). This alloy is designed to perform exceptionally well in harsh environments, particularly where exposure to seawater, brine, and various chemicals is common.
Key Features:
- Composition: The high nickel and copper content ensures outstanding resistance to corrosion, while titanium and iron contribute to enhanced strength and hardness.
- Strength and Hardness: Monel 505 offers high tensile strength of approximately 760 MPa (110 ksi) and a yield strength of around 310 MPa (45 ksi). The Rockwell C hardness is about 35, which provides durability and resistance to wear.
- Corrosion Resistance: The alloy excels in resisting corrosion from seawater, brine, and a range of aggressive chemicals, making it ideal for marine and chemical processing applications.
- Temperature Performance: Monel 505 maintains its mechanical properties and resistance to deformation at elevated temperatures, adding to its versatility in high-temperature environments.
- Applications: Commonly used in marine hardware, aerospace components, and chemical processing equipment. Its high strength and resistance to corrosive environments make it suitable for demanding industrial applications.
Monel 505’s robust combination of strength, hardness, and excellent corrosion resistance makes it a preferred choice for applications requiring durability and reliability in challenging conditions.
Here is a detailed composition table for Monel 505 Alloy:
| Element | Percentage |
|---|---|
| Nickel (Ni) | 63% |
| Copper (Cu) | 31% |
| Iron (Fe) | ≤2.5% |
| Manganese (Mn) | ≤1.5% |
| Titanium (Ti) | 0.35-0.85% |
| Carbon (C) | ≤0.3% |
| Sulfur (S) | ≤0.01% |
| Silicon (Si) | ≤0.5% |
This composition ensures Monel 505’s high strength and excellent resistance to corrosion.